The dissolution of α-FePO4 and
the α-Ga0.75Fe0.25PO4 solid solution with
α-quartz-type structures under hydrothermal conditions in 1 M HNO3 aqueous solution was
investigated by in situ X-ray absorption spectroscopy (XAS) at the Fe
K-edge.The solubility of α-FePO4 increases with temperature and is
higher at 25 MPa than at 50 MPa.The Fe3+ cation in solution is
6-fold coordinated with an average Fe–O distance close to 2.0 Å.A similar
experiment was performed with a solid solution of α-quartz-type Ga0.75Fe0.25PO4
as the starting phase under a pressure of 25 MPa.By varying the temperature
from 303 K up to 573 K a single crystal was grown with 23% Fe3+ with
the α-quartz-type structure.These results show that the crystallization of
pure α-quartz-type FePO4 by the hydrothermal method is not possible
due to the formation of very stable Fe3+ hexa-aquo complexes [Fe(H2O)6]3+
and to the absence of FeO4 tetrahedra in solution.Ga3+
cations in solution induce the formation of gallophosphate complexes at the
solid–liquid interface,which are at the origin of the nuclei for
crystallization.We propose a crystallization mechanism in which the Fe3+
substitutes Ga3+ with a 4-fold coordination in mixed (iron/gallo)-phosphate
complexes that leads to the growth of an α-quartz-type Ga0.77Fe0.23PO4
single crystal.
The dissolution of α-FePO4 and
the α-Ga0.75Fe0.25PO4 solid solution with
α-quartz-type structures under hydrothermal conditions in 1 M HNO3 aqueous solution was
investigated by in situ X-ray absorption spectroscopy (XAS) at the Fe
K-edge.The solubility of α-FePO4 increases with temperature and is
higher at 25 MPa than at 50 MPa.The Fe3+ cation in solution is
6-fold coordinated with an average Fe–O distance close to 2.0 Å.A similar
experiment was performed with a solid solution of α-quartz-type Ga0.75Fe0.25PO4
as the starting phase under a pressure of 25 MPa.By varying the temperature
from 303 K up to 573 K a single crystal was grown with 23% Fe3+ with
the α-quartz-type structure.These results show that the crystallization of
pure α-quartz-type FePO4 by the hydrothermal method is not possible
due to the formation of very stable Fe3+ hexa-aquo complexes [Fe(H2O)6]3+
and to the absence of FeO4 tetrahedra in solution.Ga3+
cations in solution induce the formation of gallophosphate complexes at the
solid–liquid interface,which are at the origin of the nuclei for
crystallization.We propose a crystallization mechanism in which the Fe3+
substitutes Ga3+ with a 4-fold coordination in mixed (iron/gallo)-phosphate
complexes that leads to the growth of an α-quartz-type Ga0.77Fe0.23PO4
single crystal.
α-磷酸铁和α-Ga0.75Fe0.25PO4固溶体以及α-石英型结构在1摩尔硝酸水溶液中的溶解情况在高温的条件下于反应过程中经由X-射线吸收光谱(XAS)在 Fe K-边缘 分析.α-磷酸铁的可溶性随着温度的提高而提高,压强25兆帕时高于压强50兆帕.Fe3+ 阳离子的协调性增加了6倍,Fe–O 之间的距离接近 2.0 埃. 类似的实验曾经在压强为25兆帕的状况下做过,其中作为启动阶段的固溶体是Ga0.75Fe0.25PO4 和 α-石英型结构.当 把温度从303 K 上升到573 K 时,23% Fe3+ 和 α-石英型结构析出了一颗单晶.以上的实验结果显示,由于有非常稳定的水和复合物[Fe(H2O)6]3+的形成以及缺少FeO4四面体,用高温处理的办法从而形成纯α-石英型结构FePO4是不可行的.溶液里的Ga3+阳离子的存在促使镓磷酸盐复合物在固体和液体界面形成,这是形成结晶的原因.我们建议
用Fe3+离子代替Ga3+,并且在(铁/加洛)磷酸酯复合物里用4倍的协调性,这样,就会产生一颗α-石英型Ga0.77Fe0.23PO4的单晶.
累死我了.6-fold coordination 和 4-fold coordiation 不知道是什么东西,实在帮不了你了.
用Fe3+离子代替Ga3+,并且在(铁/加洛)磷酸酯复合物里用4倍的协调性,这样,就会产生一颗α-石英型Ga0.77Fe0.23PO4的单晶.
累死我了.6-fold coordination 和 4-fold coordiation 不知道是什么东西,实在帮不了你了.
英语翻译The dissolution of α-FePO4 andthe α-Ga0.75Fe0.25PO4 soli
英语翻译the dissolution capacity of the solvent is directly link
We do the dissolution of
The formation ,maintenance ,and dissolution of the family ar
There are two doors ,one of which__to the living room andthe
英语翻译3、we have lunch in the cafe in the park.andthe food asn'
英语翻译1.Materials simply are atoms joined together in the soli
英语翻译A mere “dissolution”or “partitioning”model does not expl
英语翻译He admits logistics has multiple meanings andthe service
I dig the soli ahd put it in the sun every day
英语翻译Do you know that animals have love for each other andthe
英语翻译It's raining andthe town seems totally forgotten by peop